UHP Graphite electrode
Incazelo
Ama-electrode e-graphite anamandla aphezulu enziwe nge-coke yenaliti yekhwalithi ephezulu njengeyona nto eyinhloko eluhlaza, futhi enziwa ngokwakhiwa, ukugazinga, ukukhulelwa, i-graphitizing kanye nokucubungula ngomshini.Zisetshenziswa kabanzi kuma-arc kagesi njengezinto zokuhambisa.
Ukucaciswa
Izinkomba zomzimba namakhemikhali zama-electrode e-graphite ezinamandla aphezulu kanye nezingono zibhekisela ku-YB/T 4090-2015
Imiyalo ye-graphite electrode
1.Ama-Electrode kufanele agcinwe endaweni ehlanzekile, eyomile, ukugwema ukushaqeka nokushayisana.Kufanele omiswe ngaphambi kokuba usetshenziswe.
2.Uma uhlanganisa izingono, hlanza imbobo ngomoya ocindezelekile, bese ugoqa izingono kuwo ngemoto ngaphandle kokulimaza izintambo.
3.Ngaphambi kwethiphu ye-electrode ngomoya ocindezelwe lapho ama-electrode amabili ekude ngo-20-30mm.
4.Lapho ama-electrode exhunywe ama-wrenches, kufanele aqiniswe ngokugcwele ku-lacation ecacisiwe ukuthi igebe phakathi kwama-electrode amabili lingaphansi kuka-0.005mm.
5. Ukuze ugweme ukuphuka kwe-electrode, sicela uqhelelane namabhulokhi wezinto zokufundisa.
6.Ukuze ugweme ukuphuka kwe-electrode, beka ibhulokhi ye-aniseed engxenyeni engezansi bese usetha ibhulokhi encane engxenyeni engenhla.
| Iphrojekthi | Ububanzi begama/mm | ||||
| 300-400 | 450 ~ 500 | 550 ~ 650 | 700~800 | ||
| Ukungazweli /μΩ·m≤ | I-Electrode | 6.2 | 6.3 | 6.0 | 5.8 |
| Ingono | 5.3 | 5.3 | 4.5 | 4.3 | |
| Amandla e-Flexural/MPa≥ | I-Electrode | 10.5 | 10.5 | 10.0 | 10.0 |
| Ingono | 20.0 | 20.0 | 22.0 | 23.0 | |
| I-Elastic Modulus /GPa≤ | I-Electrode | 14.0 | 14.0 | 14.0 | 14.0 |
| Ingono | 20.0 | 20.0 | 22.0 | 22.0 | |
| Ukuminyana kwenqwaba /(g/cm3)≥ | I-Electrode | 1.67 | 1.66 | 1.66 | 1.68 |
| Ingono | 1.74 | 1.75 | 1.78 | 1.78 | |
| I-coefficient yokwandisa ukushisa /(10-6/℃)≤ (izinga lokushisa ekamelweni ~ 600℃） | I-Electrode | 1.5 | 1.5 | 1.5 | 1.5 |
| Ingono | 1.4 | 1.4 | 1.3 | 1.3 | |
| Umlotha /％ ≤ | 0.5 | 0.5 | 0.5 | 0.5 | |
| Qaphela: Umlotha uhlukaniswe waba inkomba yereferensi. | |||||